Deep-UV optical gain in AlGaN-based gradedindex separate confinement heterostructure Emanuele Francesco Pecora1,2,3 Haiding Sun1,3 Luca Dal Negro, Theodore D. Moustakas1,* 1

Department of Electrical and Computer Engineering and Photonics Center, Boston University, 8 Saint Mary’s Street, Boston, Massachusetts 02215, USA 2 now at: Stanford University, Geballe Laboratory for Advanced Materials, Stanford, CA 94305, USA 3 contributed equally *[email protected]

Abstract: We propose AlGaN-based GRaded-INdex Separate Confinement Heterostructure as a candidate for electrically pumped deep-UV semiconductor laser. Strong compositional fluctuations were introduced in the active region (75 nm-thick Al0.72Ga0.28N film grown by RF Plasmaassisted Molecular Beam Epitaxy) to obtain net modal optical gain peaked at 257 nm in excess of 80 cm−1. We measured an optical gain threshold of 14 µJ/cm2. Because of polarization-doping of the compositionally graded AlGaN regions, which automatically leads to the formation of p-i-n junction, these results pave the way for lasing under electrical injection. © 2015 Optical Society of America OCIS codes: (140.4780) Optical resonators; (160.3380) Laser materials; (310.6860) Thin films, optical properties; (320.7100) Ultrafast measurements.

References and links 1.

F. A. Ponce and D. B. Bour, “Nitride-based semiconductors for blue and green light-emitting devices,” Nature 386(6623), 351–359 (1997). 2. S. F. Chichibu, A. Uedono, T. Onuma, B. A. Haskell, A. Chakraborty, T. Koyama, P. T. Fini, S. Keller, S. P. Denbaars, J. S. Speck, U. K. Mishra, S. Nakamura, S. Yamaguchi, S. Kamiyama, H. Amano, I. Akasaki, J. Han, and T. Sota, “Origin of defect-insensitive emission probability in In-containing (Al,In,Ga)N alloy semiconductors,” Nat. Mater. 5(10), 810–816 (2006). 3. A. Khan, K. Balakrishnan, and T. Katona, “Ultraviolet light-emitting diodes based on group three nitrides,” Nat. Photonics 2(2), 77–84 (2008). 4. C. Pernot, M. Kim, S. Fukahori, T. Inazu, T. Fujita, Y. Nagasawa, A. Hirano, M. Ippommatsu, M. Iwaya, S. Kamiyama, I. Akasaki, and H. Amano, “Improved Efficiency of 255–280 nm AlGaN-Based Light-Emitting Diodes,” Appl. Phys. Express 3(6), 061004 (2010). 5. H. Hirayama, Y. Tsukada, T. Maeda, and N. Kamata, “Marked Enhancement in the Efficiency of DeepUltraviolet AlGaN Light-Emitting Diodes by Using a Multiquantum-Barrier Electron Blocking Layer,” Appl. Phys. Express 3(3), 031002 (2010). 6. R. Grandusky, S. R. Gibb, M. C. Mendrick, C. Moe, M. Wraback, and L. J. Schowalter, “High Output Power from 260 nm Pseudomorphic Ultraviolet Light-Emitting Diodes with Improved Thermal Performance,” Appl. Phys. Express 4(8), 082101 (2011). 7. J. Mickevicius, G. Tamulaitis, M. Shur, M. Shatalov, J. Yang, and R. Gaska, “Internal quantum efficiency in AlGaN with strong carrier localization,” Appl. Phys. Lett. 101(21), 211902 (2012). 8. A. Bhattacharyya, T. D. Moustakas, L. Zhou, D. J. Smith, and W. Hug, “Deep ultraviolet emitting AlGaN quantum wells with high internal quantum efficiency,” Appl. Phys. Lett. 94(18), 181907 (2009). 9. T. D. Moustakas, Y. Liao, C. Kao, C. Thomidis, A. Bhattacharyya, D. Bhattarai, and A. Moldawer, “Deep UVLEDs with high IQE based on AlGaN alloys with strong band structure potential fluctuations,” Proc. SPIE. 8278, 82780L (2012). 10. Y. Liao, C. Thomidis, C. K. Kao, and T. D. Moustakas, “AlGaN based deep ultraviolet light emitting diodes with high internal quantum efficiency grown by molecular beam epitaxy,” Appl. Phys. Lett. 98(8), 081110 (2011). 11. W. Zhang, A. Yu. Nikiforov, C. Thomidis, J. Woodward, H. Sun, C. K. Kao, D. Bhattarai, A. Moldawer, L. Zhou, D. J. Smith, and T. D. Moustakas, “Molecular beam epitaxy growth of AlGaN quantum wells on 6H-SiC substrates with high internal quantum efficiency,” J. Vac. Sci. Technol. B 30, 02B119 (2012).

#233457 - $15.00 USD (C) 2015 OSA

Received 29 Jan 2015; revised 5 Mar 2015; accepted 5 Mar 2015; published 17 Mar 2015 1 Apr 2015 | Vol. 5, No. 4 | DOI:10.1364/OME.5.000809 | OPTICAL MATERIALS EXPRESS 809

12. C. Himwas, R. Songmuang, L. S. Dang, J. Bleuse, L. Rapenne, E. Sarigiannidou, and E. Monroy, “Thermal stability of the deep ultraviolet emission from AlGaN/AlN Stranski-Krastanov quantum dots,” Appl. Phys. Lett. 101(24), 241914 (2012). 13. T. Oto, R. G. Banal, K. Kataoka, M. Funato, and Y. Kawanishi, “100 mW deep-ultraviolet emission from aluminium-nitride-based quantum wells pumped by an electron beam,” Nature Phot. 4(11), 767–770 (2010). 14. M. Shatalov, W. Sun, A. Lunev, X. Hu, A. Dobrinsky, Y. Bilenko, J. Yank, M. Shur, R. Gaska, C. Moe, G. Garrett, and M. Wraback, “AlGaN Deep-Ultraviolet Light-Emitting Diodes with External Quantum Efficiency above 10%,” Appl. Phys. Express 5(8), 082101 (2012). 15. T. Takano, Y. Narita, A. Horiuchi, and H. Kawanishi, “Room-temperature deep-ultraviolet lasing at 241.5 nm of AlGaN multiple-quantum-well laser,” Appl. Phys. Lett. 84, 3567 (2004). 16. T. Wunderer, C. L. Chua, Z. Yang, J. E. Northrup, N. M. Johnson, G. A. Garrett, H. Shen, and M. Wraback, “Pseudomorphically Grown Ultraviolet C Photopumped Lasers on Bulk AlN Substrates,” Appl. Phys. Express 4(9), 092101 (2011). 17. E. F. Pecora, W. Zhang, A. Yu. Nikiforov, L. Zhou, D. J. Smith, J. Yin, R. Paiella, L. Dal Negro, and T. D. Moustakas, “Sub-250 nm room-temperature optical gain from AlGaN/AlN multiple quantum wells with strong band-structure potential fluctuations,” Appl. Phys. Lett. 100, 061111 (2012). 18. J. Mickevicius, J. Jurkevicius, K. Kazlauskas, A. Zakauskas, G. Tamulaitis, M. S. Shur, M. Shatalov, J. Yang, and R. Gaska, “Stimulated emission in AlGaN/AlGaN quantum wells with different Al content,” Appl. Phys. Lett. 100(8), 081902 (2012). 19. T. Wunderer, C. L. Chua, J. E. Northrup, Z. Yang, N. M. Johnson, M. Kneissl, G. A. Garrett, H. Shen, M. Wraback, B. Moody, H. S. Craft, R. Schlesser, R. F. Dalmau, and Z. Sitar, “Optically pumped UV lasers grown on bulk AlN substrates,” Phys. Status Solidi C 9(3-4), 822–825 (2012). 20. V. N. Jmerik, E. V. Lutsenko, and S. V. Ivanov, “Plasma-assisted molecular beam epitaxy of AlGaN heterostructures for deep-ultraviolet optically pumped lasers,” Phys. Status Sol. A 210(3), 439–450 (2013). 21. Z. Lochner, T. Kao, Y. Liu, X. Li, M. M. Satter, S. Shen, P. D. Yoder, J. Ryou, R. D. Dupuis, Y. Wei, H. Xie, A. Fischer, and F. A. Ponce, “Deep-ultraviolet lasing at 243 nm from photo-pumped AlGaN/AlN heterostructure on AlN substrate,” Appl. Phys. Lett. 102(10), 101110 (2013). 22. J. Xie, S. Mita, Z. Bryan, W. Guo, L. Hussey, B. Moody, R. Schlesser, R. Kirste, M. Gerhold, R. Collazo, and Z. Sitar, “Lasing and longitudinal cavity modes in photo-pumped deep ultraviolet AlGaN heterostructures,” Appl. Phys. Lett. 102(17), 171102 (2013). 23. M. Martens, F. Mehnke, C. Kuhn, C. Reich, V. Kueller, A. Knauer, C. Netzel, C. Hartmann, J. Wollweber, J. Rass, T. Wernicke, M. Bickermann, M. Weyers, and M. Kneissl, “Performance Characteristics of UV-C AlGaNBased Lasers Grown on Sapphire and Bulk AlN Substrates,” Photonics Technology Letters, IEEE 26(4), 342– 345 (2014). 24. Y. Liu, Z. Lochner, T. Kao, M. M. Satter, X. Li, J. Ryou, S. Shen, P. D. Yoder, T. Detchprohm, R. D. Dupuis, Y. Wei, H. Xie, A. Fischer, and F. Ponce, “Optically pumped AlGaN quantum-well lasers at sub-250 nm grown by MOCVD on AlN substrates,” Phys. Status Solidi C 11(2), 258–260 (2014). 25. T. Oto, R. G. Banal, M. Funato, and Y. Kawakami, “Optical gain characteristics in Al-rich AlGaN/AlN quantum wells,” Appl. Phys. Lett. 104(18), 181102 (2014). 26. W. Guo, Z. Bryan, J. Xie, R. Kirste, S. Mita, I. Bryan, L. Hussey, M. Bobea, B. Haidet, M. Gerhold, R. Collazo, and Z. Sitar, “Stimulated emission and optical gain in AlGaN heterostructures grown on bulk AlN substrates,” J. Appl. Phys. 115(10), 103108 (2014). 27. X. H. Li, T. Detchprohm, T. Kao, M. M. Satter, S. Shen, P. D. Yoder, R. D. Dupuis, S. Wang, Y. O. Wei, H. Xie, A. M. Fischer, F. A. Ponce, T. Wernicke, C. Reich, M. Martens, and M. Kneissl, “Low-threshold stimulated emission at 249 nm and 256 nm from AlGaN-based multiple-quantum-well lasers grown on sapphire substrates,” Appl. Phys. Lett. 105(14), 141106 (2014). 28. E. F. Pecora, W. Zhang, A. Yu. Nikiforov, J. Yin, R. Paiella, L. Dal Negro, and T. D. Moustakas, “Sub-250 nm light emission and optical gain in AlGaN materials,” J. Appl. Phys. 113, 013106 (2013). 29. W. T. Tsang, “Extremely low threshold (AlGa)As modified multiquantum well heterostructure lasers grown by molecular-beam epitaxy,” Appl. Phys. Lett. 39(10), 786–788 (1981). 30. W. T. Tsang, “Extremely low threshold (AlGa)As graded-index waveguide separate-confinement heterostructure lasers grown by molecular beam epitaxy,” Appl. Phys. Lett. 40(3), 217–219 (1982). 31. D. Kasemset, C.-S. Hong, N. B. Patel, and P. D. Dapkus, “Graded barrier single quantum well lasers - Theory and experiment,” IEEE J. Quantum Electron. 19(6), 1025–1030 (1983). 32. H. Sun, J. Woodward, J. Yin, A. Moldawer, E. F. Pecora, A. Yu. Nikiforov, L. Dal Negro, R. Paiella, K. Ludwig, Jr., D. J. Smith, and T. D. Moustakas, “Development of AlGaN-Based Graded-Index-SeparateConfinement Heterostructure Deep UV Emitters by Molecular Beam Epitaxy,” J. Vac. Sci. Technol. B 31, 03C117 (2013). 33. T. D. Moustakas and A. Bhattacharyya, “(Invited) Experimental Evidence that the Plasma-Assisted MBE Growth of Nitride Alloys is a Liquid Phase Epitaxy Process,” ECS Trans. 35, 63–71 (2011). 34. T. D. Moustakas and A. Bhattacharyya, “The role of liquid phase epitaxy during growth of AlGaN by MBE,” Phys. Status Solidi C 9(3-4), 580–583 (2012). 35. T. D. Moustakas, “The role of extended defects on the performance of optoelectronic devices in nitride semiconductors,” Phys. Status Solidi A 210(1), 169–174 (2013).

#233457 - $15.00 USD (C) 2015 OSA


36. A. Pinos, V. Liuolia, S. Marcinkevičius, J. Yang, R. Gaska, and M. S. Shur, “Localization potentials in AlGaN epitaxial films studied by scanning near-field optical spectroscopy,” J. Appl. Phys. 109(11), 113516 (2011). 37. S. Marcinkevičius, R. Jain, M. Shatalov, J. Yang, M. Shur, and R. Gaska, “High spectral uniformity of AlGaN with a high Al content evidenced by scanning near-field photoluminescence spectroscopy,” Appl. Phys. Lett. 105(24), 241108 (2014). 38. D. Brunner, H. Angerer, E. Bustarret, F. Freudenberg, R. Hopler, R. Dimitrov, O. Ambacher, and M. Stutzmann, “Optical constants of epitaxial AlGaN films and their temperature dependence,” J. Appl. Phys. 82(10), 5090– 5096 (1997). 39. H. Yoshida, M. Kuwabara, Y. Yamashita, Y. Takagi, K. Uchiyama, and H. Kan, “AlGaN-based laser diodes for the short-wavelength ultraviolet region,” New J. Phys. 11(12), 125013 (2009). 40. H. Yoshida, Y. Yamashita, M. Kuwabara, and H. Kan, “A 342-nm ultraviolet AlGaN multiple-quantum-well laser diode,” Nat. Photonics 2(9), 551–554 (2008). 41. K. L. Shaklee, R. E. Nahory, and R. F. Leheny, “Optical gain in semiconductors,” J. Lumin. 7, 284–309 (1973). 42. L. Dal Negro, M. Cazzanelli, L. Pavesi, S. Ossicini, D. Pacifici, G. Franzò, F. Priolo, and F. Iacona, “Dynamics of stimulated emission in silicon nanocrystals,”Appl. Phys. Lett. 82, 4636 (2003). 43. G. Frankowsky, F. Steuber, V. Harle, F. Scholz, and A. Hangleiter, “Tailoring the dielectric properties of HfO2– Ta2O5 nanolaminates,” Appl. Phys. Lett. 68, 3746 (1996). 44. M. Röwe, M. Vehse, P. Michler, J. Gutowski, S. Heppel, and A. Hangleiter, “Optical gain, gain saturation, and waveguiding in group III-nitride heterostructures,” Phys. Status Solidi, C Conf. Crit. Rev. 0(6), 1860–1877 (2003). 45. L. Dal Negro, P. Bettotti, M. Cazzanelli, D. Pacifici, and L. Pavesi, "Applicability conditions and experimental analysis of the variable stripe length method for gain measurements,” Opt. Commun. 229, 337–348 (2004). 46. Z. E. Lambert, S. E. Lappi, J. M. Papanikolas, and C. L. Reynolds, Jr., “Intrinsic optical gain in thin films of a conjugated polymer under picosecond excitation,” Appl. Phys. Lett. 103, 033303 (2013). 47. E. F. Pecora, W. Zhang, J. Yin, R. Paiella, L. Dal Negro, and T. D. Moustakas, “Polarization Properties of DeepUltraviolet Optical Gain in Al-Rich AlGaN Structures,” Appl. Phys. Express 5(3), 032103 (2012). 48. J. E. Northrup, C. L. Chua, Z. Yang, T. Wunderer, M. Kneissl, N. M. Johnson, and T. Kolbe, “Effect of strain and barrier composition on the polarization of light emission from AlGaN/AlN quantum wells,” Appl. Phys. Lett. 100(2), 021101 (2012). 49. J. Zhang, H. Zhao, and N. Tansu, “Effect of crystal-field split-off hole and heavy-hole bands crossover on gain characteristics of high Al-content AlGaN quantum well lasers,” Appl. Phys. Lett. 97(11), 111105 (2010). 50. A. A. Yamaguchi, “Theoretical investigation of optical polarization properties in Al-rich AlGaN quantum wells with various substrate orientations,” Appl. Phys. Lett. 96(15), 151911 (2010). 51. S. Park, “Al Composition Dependence of the Optical Gain Characteristics of a-plane Al-rich AlGaN/AlN Quantum-well Structures,” J. Korean Phys. Soc. 59, 357–361 (2011). 52. V. I. Klimov, A. A. Mikhailovsky, S. Xu, A. Malko, J. A. Hollingsworth, C. A. Leatherdale, H. Eisler, and M. G. Bawendi, “Optical gain and stimulated emission in nanocrystal quantum dots,” Science 290(5490), 314–317 (2000). 53. Y. Arakawa, Proc. CLEO 2012 JM4I, JM4I.3 (2012).

1. Introduction The demonstration of a compact, portable, solid-state deep-UV laser is strongly required to enable a number of applications in different fields, such as non-line-of-sight free-space optical

#233457 - $15.00 USD (C) 2015 OSA


Fig. 1. Schematic of the investigated GRINSCH double heterostructure.

communications, biochemical agent detection, disinfection, and medical diagnostics. GaN alloyed with high AlN mole fraction is the most promising platform for sub-250 nm electrically-injected LEDs and lasers [1, 2]. In the last few years, many groups have investigated AlGaN-based light emitting devices operating below 300 nm. The majority of the reported external quantum efficiencies of LEDs are very low so far (less than 3%) [3–7]. Nevertheless, the ability to grow high quality materials has been proven also at wavelengths down to 235 nm, exhibiting internal quantum efficiency up to 70% at 240 nm [8–12], power efficiency of 40% at 240 nm [13], and, more recently, deep UV LEDs with external quantum efficiency above 10% [14] have been reported. Moreover, some prototypes of optically pumped deep-UV lasers as well as the demonstration of stimulated emission have been reported in the literature [15–27]. The employment of multiple quantum well structures is one of the most effective approaches for obtaining lasing. However, homogeneous quantum wells require high carrier density to invert their population before any stimulated emission process sets in. In order to overcome this issue, the authors have already proposed to take advantage of strong band-structure potential fluctuations to lower the threshold gain and increase the net modal gain [17, 28]. An alternative approach consists in the design of a laser structure capable of enhancing both the carrier and the optical confinement factors in the active region. Semiconductor laser designs have evolved extensively over the last few decades targeting lower lasing thresholds with higher gain efficiency. These important performance indicators were demonstrated via several architectural improvements, which include the Separate Confinement Heterostructure (SCH) laser, the quantum well SCH, and the GRaded-INdex SCH (GRINSCH) geometry [29–31]. Unlike conventional heterostructures, in a GRINSCH laser the cladding materials are progressively alloyed so that the band gap of the cladding is reduced to match the band gap of the material with the smallest gap. As a result, the GRINSCH design not only efficiently confines carriers but also enhances the optical confinement factor [29–32]. In this paper, we report the development of an AlGaN-based deep-UV laser structure in the form of a GRaded INdex Separate Confinement Heterostructure (GRINSCH), which is capable of better carrier and optical confinement. We demonstrate that our approach is able to efficiently inject the photo-excited electrons and holes into the active layer (AlGaN, 72% Al content, grown by RF plasma-assisted Molecular Beam Epitaxy with strong compositional fluctuation). The combination of the material properties and the designed GRINSCH structure leads to a maximum net modal gain in excess of 80 cm−1 measured by the Variable Stripe Length technique with an optical gain threshold of 14 µJ/cm2 in a 75 nm single layer active region device. Furthermore, as discussed elsewhere [32], the band diagram of this AlGaN-

#233457 - $15.00 USD (C) 2015 OSA


Fig. 2. Vertical profile of the index of refraction and numerical simulation of the optical mode intensity in the structure.

based GRINSCH structure has the form of a p-n junction due to polarization n-and p-type doping of the AlGaN graded regions on either side of the active region. Thus, this structure has the potential for the development of an electrically pumped deep UV semiconductor laser. 2. Methods The laser structures were grown by RF plasma-assisted MBE on the Si face of (0001) 6H-SiC substrates. The MBE system is equipped with an EPI Unibulb rf plasma source for the activation of nitrogen and traditional effusion cells for the evaporation of Al, Ga and In. The substrate temperature was monitored with a thermocouple, placed in the cavity behind the substrate, as well as with a pyrometer. In general, the pyrometer reading was about 100 °C lower than the thermocouple reading. The substrate preparation and film growth were monitored by reflection high-energy electron diffraction (RHEED). The SiC substrates were first cleaned ex situ in organic solvents, followed by dipping them into a heated pirana etch and then in buffered hydrofluoric acid to remove surface contaminants and oxides. In addition, the substrates were cleaned in situ by exposure to Ga flux at 750 °C for complete coverage, followed by fast heating to 850 °C for Ga desorption. This process was found to lead to a sharp √3x√3 R30 reconstruction in the RHEED pattern, which was attributed to the removal of oxygen, carbon, hydrogen and other chemisorbed or physibsorbed impurities through the formation of volatile Ga compounds. The structure consists of a 500 nm AlN cladding layer, followed by a 50 nm AlxGa1-xN linearly graded from x = 1 to x = 0.8. The active region of the device consists of 75 nm of Al0.72Ga0.28N film, followed by the 50 nm AlxGa1-xN linearly graded from x = 0.8 to x = 1 and 100 nm AlN cladding layer (see Fig. 1). Indium was used as a surfactant during the growth of the graded AlGaN layers in order to improve their crystal quality. We have previously reported [32] a density of threading dislocations under these growth conditions of about 108 cm−2. Moreover, we measured a RMS roughness of 0.79 nm on a 2µm x 2µm AFM image. The active region was grown under Garich conditions, a growth mode that promotes the development of compositional inhomogeneities leading to deep band structure potential fluctuations [17, 28, 33–35]. It has been already demonstrated that nanoscale fluctuations are mainly responsible for light emission in these materials [17] and of the inhomogeneous broadening of the AlGaN emission [36, 37]. On the other hand, we note that the employment of Indium as a surfactant removes the compositional inhomogeneities as revealed by cathodoluminescence measurements [28]. As a consequence, these nanoscale fluctuations are not present in the graded composition regions, which have no role on the light emission of the structure. As will be discussed later, the optical mode here is TM polarized and its optical-mode confinement in the GRINSCH double hetero-structure, described in Fig. 1, was determined using a commercially available

#233457 - $15.00 USD (C) 2015 OSA


Fig. 3. Measured edge emission spectrum intensity (log scale) normalized by the excitation fluence as a function of the wavelength. (Inset) ASE peak intensity as a function of the analyzer angle. 0° corresponds to the s polarization of the emission (TM mode); 90° to the p polarization (TE mode).

simulation tool (Comsol Multiphysics). Figure 2 shows the vertical profile of the index of refraction and optical mode. Refractive indices at an emission wavelength of 257 nm of 2.3766, 2.4684 and 2.70439 - 0.3277 x (0.8 ≤ x ≤ 1) were used for the AlN, Al0.72Ga0.28N and graded AlxGa1-xN layers respectively [38]. As illustrated by the calculated transverse mode profile, the optical mode was well confined by the graded AlGaN film, with an optical confinement factor, Γ, in the active region of the device of 32.5%, which is a significant improvement over the reported 1~3% for most InGaN and AlGaN MQW-based lasers [39, 40]. The optical properties and gain of the designed laser structure have been investigated through the Variable Stripe Length (VSL) technique. It is a very reliable and widely used method for the measurement of the optical gain coefficient in bulk materials. This approach allows measuring unambiguously the net modal gain coefficient and the entire gain spectrum [41–44]. No special sample preparation is needed; however some experimental conditions need to be carefully verified to avoid any artifacts [45]. Data are analyzed within the 1D amplifier model to determine the net modal gain/absorption coefficient. The sample has been excited with 220 nm laser pulses, obtained by pumping a proper fourth-harmonic generation crystal (Spectra Physics GWU-24FL) with a mode-locked ultra-fast high-power Ti:sapphire laser (SpectraPhysics MaiTai, 150 fs pulse width, 82 MHz repetition rate) operating at 880 nm. The pulse separation (12 ns) is much larger than the typical emission lifetime in these systems (few nanoseconds), while the laser pulses have a temporal width shorter than the PL decay time. The combination of these conditions corresponds to a transient single pulse excitation regime. This is not an uncommon choice for probing the potential of novel laser materials. In particular, Amplified Spontaneous Emission (ASE) and gain in AlGaN systems have always been observed in a single pulse excitation regime [15, 16, 19, 23, 24]. Moreover, it has been demonstrated that optical gain can be observed and measured also under these conditions, which represent a more accurate representation of the intrinsic net gain [46]. The laser pulses were focused on the sample surface through a cylindrical lens forming a stripe whose length can be monitored and adjusted through a blade mounted in a motorized computer-controlled stage. The beam profile along the stripe has been measured through the knife-edge technique, resulting in a height of the stripe of 5 µm and a maximum stripe length of 250 µm, which provides a homogeneous illumination of the sample. Beyond this area the pumping intensity cannot be considered uniform anymore and VSL gain data should not be trusted [45, 47]. The maximum fluence on the sample is 60 µJ/cm2. The ASE has been

#233457 - $15.00 USD (C) 2015 OSA


Fig. 4. (a) ASE intensity measured at the fixed wavelength of 257 nm (the peak wavelength) as a function of the pumping fluence. (b) VSL traces collected at different pumping fluences. (c) The entire set of measured net modal gain values as a function of the pumping fluence.

collected from the cleaved edge of the sample through an UV-transmitting objective, an UVtransmitting movable analyzer, a computer-controlled f/4 monochromator (Cornerstone 260) with UV-efficient gratings, and a lock-in amplifier (Oriel Merlin) coupled to a UV-optimized photomultiplier tube (Oriel Instruments 77348). 3. Discussion In Fig. 3 we report the measured edge emission spectrum intensity normalized by the excitation fluence as a function of the wavelength. This normalization better emphasizes the super-linear behavior of the emitted intensity. All the spectra would line up if the edgeemission depended linearly on the pumping fluence. On the other hand, we observe that the intensities of the edge-emission spectra evolve non-linearly with the pumping fluence. This behavior corresponds to the super-linear Amplified Spontaneous Emission (ASE) from the sample. We do not observe any significant spectral shift within the accessible fluency range. We have also investigated the polarization properties of the ASE emission in order to better understand the origin of the observed luminescence and gain. In the polar plot shown in the inset of Fig. 3, we report the peak intensity as a function of the analyzer angle. 0° corresponds to the s polarization of the emission (TM mode); 90° to the p polarization (TE mode). Intensities have been recorded at the highest pump fluence (60 µJ/cm2) and they are reported on a linear scale. The emission from the GRINSCH structure appears strongly TM polarized. It is well known that the ASE polarization in AlGaN materials depends on a number of parameters, such as the Al content, the strain in the active layer, and its thickness [49–51]. In particular, a turnover from the TE to the TM polarization is expected for an Al content of 60-80%, depending on the actual device structure [50–52]. Our result is consistent with what has been already observed in the literature for similar Al composition [48]. It should be stressed also that the active region in our structure is not a quantum well, due to its

#233457 - $15.00 USD (C) 2015 OSA


large thickness, so we do not expect any contribution to the polarization shift due to the strain, contrary to what we have previously observed in quantum wells with similar Al composition [47]. We report in Fig. 4(a) the ASE intensity measured at the fixed wavelength of 257 nm (the peak wavelength) as a function of the pumping fluence. The measured intensity has a clear non-linear trend, and threshold fluence can be established at around 14 µJ/cm2. This is strong evidence supporting the occurrence of stimulated emission in our structure. Furthermore, all the spectra exhibit a single peak and no secondary peaks are observed at longer or shorter wavelengths, indicating that no other luminescent centers are present either in the active or in the graded region of the sample. In Fig. 4(b) we report the VSL traces collected at different pumping fluences. Data are normalized for a better comparison. Continuous lines represent the best fitting to the experimental data according to the model of a 1D optical amplifier system. We use this model to determine the net modal absorption/gain coefficient of the material at different pumping fluences for the same detection wavelength (257 nm). First, we should note the different character of the VSL traces with increasing pumping fluence. At the lowest fluence (5 and 12 µJ/cm2), the corresponding VSL trace is concave. The results are similar for lower fluences. As a consequence, the fitting procedure results in a negative term, i.e. modal absorption values. On the other hand, the traces turn into a convex function by only varying the excitation fluence. In particular, we determine for both 40 and 60 µJ/cm2 a positive net modal gain value. In Fig. 4(c) we report the entire set of measured net modal gain values as a function of the pumping fluence. First, it should be noted that a transition from negative to positive values occurs at 14 µJ/cm2. The optical transparency threshold indicates the onset of stimulated emission in the amplifier, and the measured value is well consistent with the one determined in Fig. 4(a) from the pump power dependence of the edge emission. Given our transient excitation regime, the effective photogenerated carrier density depends only on the pump fluence E, the absorption coefficient αP and the photon energy hνP [46]: N efftr =

Eα P hvP

Considering a typical absorption coefficient of 105 cm−1 at this wavelength [38], we estimate a density of excited carriers at gain threshold of 1.55 x 1018 cm−3. This value is quite low for a bulk material in the deep-UV wavelength range (usually in the range of low-1019 cm−3 [16, 25, 49]). However, previously reported numbers do not consider the effect of the graded structure in increasing the optical confinement factor and the carrier funneling into the active region of the device. Moreover, it has been demonstrated that using a pulse width much shorter than the PL decay time reduces the optical gain thresholds and increases the net modal gain compared with the quasi-steady state excitation conditions [46]. We note also that, contrary to what is expected for a bulk material, the net modal gain in our sample saturates for a pumping power of 20 µJ/cm2 (very close to the optical threshold). For any higher fluences, the net modal gain keeps its value at around 80 cm−1. This trend has already been observed in nanocrystal quantum dots of different materials [52, 53], and it is consistent with the presence of compositional fluctuations in the active layer of the laser structure [28]. The net modal gain eventually starts to decrease at the highest fluences most likely due to the onset of thermal effects. From the measured net modal gain and the calculated confinement factor, we estimate that the material gain for these bulk Al0.72Ga0.28N films is about 250 cm−1. We have reported previously [17, 28] that Al0.72Ga0.28N /AlN multiple quantum wells (MQWs) have a net modal gain of about 125 cm−1. Since the confinement factor for such MQWs is of the order of 1-2%, the estimated materials gain for such MQWs is of the order of 6,000 to about 12,000 cm−1. The superior gain properties of the MQWs compared to bulk films of similar composition are

#233457 - $15.00 USD (C) 2015 OSA


attributed to better carrier confinement in the MQWs, which prevents them from diffusing and recombining at non-radiative recombination centers. Based on this discussion, we anticipate that the proposed GRINSCH structure will have even higher optical gain if the active region is made of a single or multiple AlGaN quantum wells. 4. Conclusions In conclusion, we have designed a graded-index laser double heterostructure with AlGaN in the active region to enhance the optical confinement of the structure. The devices were grown by plasma-assisted MBE on the Si face or (0001) 6H-SiC substrates. We have demonstrated large optical gain at room temperature in the deep-UV wavelength range from this structure. Optical gain is demonstrated by super-linear and polarized ASE emission and quantified by VSL analysis that shows clear switching from negative (i.e., absorption) to positive gain values above a characteristic threshold pump fluence of 14 µJ/cm2. These results pave the way to the development of sub-250 nm electrically-injected laser structures. Acknowledgments The work was partially supported by NSF (ECCS-1408364) and the Defense Advanced Research Projects Agency CMUVT Program (PM: Dr. John Albrecht) under subcontract from Photon Systems Inc. (U.S. Army Cooperative Agreement No. W911NF-11-1-0034).