Effect of viscosity and electrical conductivity on the ... - Semantic Scholar

3 downloads 185 Views 913KB Size Report
Rajiv Padhye, School of Fashion and Textiles, RMIT University, Brunswick,. Victoria 3056, Australia. Email: [email protected]. Textile Research Journal.
Original article

Effect of viscosity and electrical conductivity on the morphology and fiber diameter in melt electrospinning of polypropylene

Textile Research Journal 83(6) 606–617 ! The Author(s) 2013 Reprints and permissions: sagepub.co.uk/journalsPermissions.nav DOI: 10.1177/0040517512458347 trj.sagepub.com

Rajkishore Nayak1, Rajiv Padhye1, Ilias Louis Kyratzis2, Yen Bach Truong2 and Lyndon Arnold1

Abstract The feasibility of fabricating polypropylene (PP) nanofibers has been explored by using different additives, such as sodium oleate (SO), poly(ethylene glycol) (PEG) and poly(dimethyl siloxane) (PDMS), during melt electrospinning. PP of high melt flow index (1000) was used with PEG and PDMS for the reduction of the melt viscosity; and it was used with SO for improving the electrical conductivity during melt electrospinning. It was observed that all the additives used in this study helped to reduce the fiber diameter. The most promising additive, SO, was effective in reducing the fiber diameter to the nanometer scale due to the increase in the electrical conductivity. The fiber diameter was decreased by the addition of PEG and PDMS due to the decrease in the melt viscosity. The effect of die shape on the fiber cross-sectional shape was analyzed and an interesting finding is that the die shapes did not have an effect on the cross-sectional shape of the fibers. That is, irrespective of the die shapes (i.e. trilobal, tetralobal, multilobal and circular) used in this study, the crosssectional shapes of melt electrospun fibers were circular. The distribution of the additives in the fiber was analyzed by energy-dispersive X-ray analysis and was found to be uniform. Tensile tests were performed on single nanofibers with limited success, due to the problems in preparing fiber samples and successfully holding them in the jaws of the testing machine without slippage.

Keywords melt electrospinning, nanofiber, polypropylene, viscosity, electrical conductivity, tensile property

In the last two decades, increasing attention is being paid to the fabrication of nanomaterials, including nanofibers in the fiber industry. Nanofibers, fibers with diameters in nanometers, have a high specific surface-area-tovolume ratio, leading to their unique applications in protective clothing, filtration, biomaterials, electronics and other engineering areas.1–6 Electrospinning is mainly employed for the fabrication of nanofibers. It involves the stretching of a polymer fluid by the electrostatic attraction in the presence of an external electric field. It can be classified into two groups: solution electrospinning and melt electrospinning.7 Melt electrospinning has many advantages over solution electrospinning. It is cheaper, more eco-friendly and safer than solution electrospinning.8,9 The productivity of melt electrospinning is comparatively higher, since no

solvent evaporation is involved, which lead to mass loss of the starting materials.10,11 Polymers without appropriate solvents at room temperature, such as polyethylene (PE) and polypropylene (PP), can be easily melt electrospun. Melt electrospinning also favors the production of multi-component systems, such as blends and composites, as in many cases no common solvent

1 2

School of Fashion & Textiles, RMIT University, Australia CSIRO Materials Science & Engineering, Australia

Corresponding author: Rajiv Padhye, School of Fashion and Textiles, RMIT University, Brunswick, Victoria 3056, Australia. Email: [email protected]

Nayak et al.

607

(a)

(b)

CH3

(c) O

CH3(CH2)7

H

O

(CH2)7COONa

O

H H

H

n

Si CH3

n

Scheme 1. Chemical structure of the additives (a) sodium oleate, (b) poly(ethylene glycol) and (c) poly(dimethyl siloxane).

for all the components may exist.12 There is limited work reported on melt electrospinning because some limiting constraints are associated with the process, such as (i) coarser fibers are produced due to the high viscosity of the polymer melt compared to polymer solution;13 (ii) the equipment used for melt electrospinning is complex;13 (iii) the polymer melt is associated with the problem of electric discharge;14 and (iv) intrinsic difficulties associated with melt electrospinning involving high temperature setup and low conductivity of polymer melt.12 Majority of the previous research on melt electrospinning have reported the fabrication of microfibers by using PP of high molecular weights (i.e. low melt flow index (MFI)).15–18 In this study, an attempt was made to fabricate nanofibers of low molecular weight PP by lowering the melt viscosity and increasing the electrical conductivity (by using different additives). The addition of rheology modifiers to lower the viscosity of the medium in which they are used is well known in melt processing. On the basis of the information provided in the literature, it was decided to use the additives poly(ethylene glycol) (PEG)19 and poly(dimethyl siloxane) (PDMS)20 to lower the melt viscosity. The addition of ionic salts in solution electrospinning to improve the electrical conductivity has been investigated.21 However, the effect of improving the electrical conductivity of polymer melt has not been studied in melt electrospinning. Therefore, sodium oleate (SO) was used in this study to improve the electrical conductivity.22 The effect of different additives with varying percentages on the fiber diameter has been investigated. In addition, the effects of melt electrospinning die shapes, including trilobal, tetralobal, multilobal and circular, on the cross-sectional shape of resultant fibers was investigated. Furthermore, the mechanical characterization of single nanofibers was performed with limited success.

Experimental details Materials. PP of 1000 MFI (at 230 C, 21.6 N) was used for melt electrospinning. The 1000 MFI PP was synthesized by the chain scission of the base polymer

(Moplen 241R from Lyondellbasell with a MFI of 30) using the radical initiators in an extruder.23 Before melt electrospinning, the PP pellets were converted to fine powder by cryogenic (liquid nitrogen) grinding24 in a grinder (Glenmills, Model 500). The additives or rheology modifiers used for the current study include SO (British Drug House), PEG (PEG-300, Ega Chemie) and PDMS (United Chemical Technologies Inc.). The chemical structures of the additives are shown in Scheme 1. The additives were mixed thoroughly with the PP powder on the basis of percentage weight (i.e. 4, 7 and 12 wt%) prior to electrospinning, as per the information provided in the literature.20–22 Melt electrospinning equipment. The basic equipment used for melt electrospinning is shown in Figure 1. It consisted of five major components, namely the temperature controller, high-voltage power supply, heating assembly, syringe pump and collector. The temperature controller (BTC 909C) was able to control the temperature with an accuracy of  2 C. The temperature was measured using a K-type thermocouple. Negative voltage was applied to the collector using a high-voltage power supply (Spellman SL 150) with a voltage range of 0–50 kV. The heating assembly consisted of a metallic barrel of 10 mm inner diameter and 125 mm length. Heating was carried out by electrical heating elements housed inside the barrel. The equipment consisted of a digitally controlled syringe pump (PHD 2000, Harvard Apparatus). The polymer melt was pumped with a flow rate of 0.0013 ml/min through the die. Although different dies (such as 0.3 mm circular (C), 0.2 mm trilobal (T), 0.3 mm circular protruding (CP) and 0.2 mm CP) were successfully used for fiber production in preliminary experiments, the 0.2 mm CP die was mainly employed for the final investigations. The collector was a flat aluminum plate (150 mm (H)  80 mm (W)) overlaid with aluminum foil on which fibers were collected. The collector was placed at varied distances of 120, 140 and 150 mm. The barrel was preheated up to 200 C. The piston was removed and about 4 g of the powdered polymer (mixed with the additives) was loaded into the barrel and kept for about 10 min so that a homogenous melt was prepared and steady

608

Textile Research Journal 83(6)

Figure 1. Schematic of the equipment used for melt electrospinning.

state was achieved. The piston was reloaded and the delivery of the polymer melt was initiated. Characterization of fibers. The surface morphology of the electrospun fibers was analyzed using a Field Emission Scanning Electron Microscope (Philips XL30 FE-SEM) with an accelerating voltage of 30 kV. The fibers were placed on stubs and coated with iridium by using a high-resolution ion beam sputtering system. Fiber diameters were measured by an image processing software (Image J, NIST) using the SEM images. The average fiber diameter was determined from at least 150 measurements from at least 10 SEM images. The shear viscosity was measured using a rheometer (Ares) equipped with parallel plates in the dynamic mode. The shear viscosity of pure polymer and polymer with the additives were measured over a wide range of shear rates (0.1–100 s 1). Disc samples of 1 mm thickness were prepared by using the heat press for the tests. Frequency scans were performed with 20% strain at a temperature of 200 C. The electrical conductivity of pure polymer and polymer with SO was measured at 200 C by an electrometer (Keithley 2612). The configuration used for the measurement of the electrical conductivity is shown in Figure 2. A circular polymer disc, prepared by the heat press, was used. The polymer disc was melted by band heaters to the specific temperature. Two electrodes (separated by 5 mm) were dipped in the melt and connected to the electrometer. The electric current flowing between the electrodes was measured by applying a variable voltage (0–50 V). Energy-dispersive X-ray (EDX) microanalysis was used to investigate the presence of the additives by mapping the relative distribution of the elements, for example sodium (Na) for SO and Silicon (Si) for PDMS. The Philips XL30 FE-SEM used for analyzing

Figure 2. Configuration used for the measurement of electrical conductivity.

the surface morphology was also used for the EDX analysis. An accelerating voltage of 30 kV was used for all the specimens. To determine the SO and PDMS concentration on the surface of the fiber, X-ray net counts were obtained with a collection time of 500 s. All the fiber samples were carbon coated before the EDX analysis. The mechanical property of single nanofibers fabricated by melt electrospinning was tested in the Chatillon tensile tester (Chatillon TCD 200) with a load cell of 30 g. The gauge length was 10 mm and the traverse speed was 2.5 mm/min. A single nanofiber was carefully removed with the help of tweezers under the stage of a microscope from the aluminum foil and mounted onto a square paper using double-face tape and polyvinyl acetate (PVA) wood glue/Aquadhere, as described in Figure 3. During the tensile testing,

Nayak et al.

609

Figure 3. Preparation of single nanofiber for tensile testing in the Chatillon tensile tester. PVA: polyvinyl acetate.

the paper was cut on both sides after it was mounted into the jaws and only the fiber was held by the jaws.

Table 1. Specification of the dies used in the melt electrospinning

Results and discussion

Die size (mm)

Die shape C/T/CP

0.05 0.1 0.15 0.2 0.3 0.2 0.3 0.2

C C C C C T CP CP

Effect of die size and shape. Initially, the experiments were performed with different dies (at 48 kV, 200 C and a feed rate of 0.0013 ml/min), as listed in Table 1, with pure PP. The cross-sectional area of the dies was determined by using a microscope (Olympus). As a smaller nozzle diameter12 and low molecular weight of the polymer (i.e. high MFI)17 favor the formation of fibers with smaller diameter, preliminary experiments were performed with the smallest die size (0.05 mm) before moving to the larger sizes. It was found that the die sizes of 0.2 mm or lower did not produce any fiber, because the high viscosity of the polymer melt prevented the flow through the small orifice. Figure 4 shows the SEM images and fiber diameter distribution plots of the electrospun PP fibers using different dies. It can be observed from the diameter distribution plots that the 0.2 T die with the highest cross-sectional area produced the coarsest fiber, whereas the 0.2 CP die with the lowest cross-sectional area produced the finest fiber. The presence of nanofibers can be observed only in the case of the CP dies (i.e. 0.3 and 0.2 CP in Figure 4 (d) & (h)). The circular die (0.3 C) with almost the same area compared to the CP die (0.3 CP) produced only microfibers. The nanofiber fabrication in the case of CP dies could be due to the fact that the applied electric field was concentrated at the end of protrusion, whereas in circular dies (without protrusion) it is distributed in a wider area (Figure 5). The effect of die shape on the fiber cross-section using dies other than the circular, such as trilobal, tetralobal and multilobal (not listed in Table 1), was also analyzed. To the best of our knowledge, for the first time it was observed that there is no effect of the die shape on the fiber cross-section. The cross-sections of fibers fabricated by different dies are shown in Figure 6.

Cross-sectional area of die orifice (mm2)  104 a

0.64 1.62 2.84 6.64 34.03 6.17 2.55

Fiber formation No No No No Yes Yes Yes Yes

C: circular, T: trilobal and CP: circular protruding. a Area could not be measured.

It was noticed that all the dies (i.e. trilobal, tetralobal and multilobal) produced circular fibers similar to the circular dies. Normally in melt spinning, the cross-section of the fiber follows the die shape used (i.e. a trilobal die produces trilobal fibers). The shape of fibers not following the die cross-section is because of the presence of a Taylor cone, which is essential for electrospinning. When the high voltage is applied, the polymer melt is distorted into a conical object commonly known as the Taylor cone.25 As the electrospinning process starts from the Taylor cone formed at the apex of the die, the die cross-section plays no role in shaping the fiber cross-section. Effect of additives on fiber morphology and diameter. Experiments to investigate the effect of additives on the fiber diameter were performed by using the 0.2 CP die, as it produced the finest fibers out of all the dies investigated. The additives (SO, PEG and PDMS) were used at different weight percentages (i.e. wt% of 4, 7 and 12). The surface morphology and diameter distribution plots of the melt electrospun PP fibers fabricated with different additives (at 7 wt%, 48 kV, 200 C and a feed rate of 0.0013 ml/min) are shown in Figure 7.

610

Textile Research Journal 83(6)

(a)

(b)

Frequency

50 40 30

AVG

: 8.82

(d) 60

SDEV

: 1.83

50

MIN

: 2.98

MAX

: 14 70

Frequency

(c) 6 0

20 10

40 30 20

: 7.10

SDEV

: 3.45

MIN

: 0.25

MAX

: 18 43

10

0 0

2

4

0

6 8 10 12 14 16 18 20 Fiber diameter (μm)

0

2

4 6 8 10 12 14 16 18 20 Fiber diameter (μm)

(f)

(g) 6 0 50 40 30

AVG

: 7.66

SDEV

: 3.07

MIN

: 2.23

MAX

: 15 61

20

50 40 30 20

AVG

: 4.93

SDEV

: 1.84

MIN

: 0.16

MAX

: 11 87

10

10 0

(h) 6 0

Frequency

(e)

Frequency

AVG

0

2

4

8 6 10 12 14 16 18 20 Fiber diameter (μm)

0

0

2

4

6 8 10 12 14 16 18 20 Fiber diameter (μm)

Figure 4. Scanning electron micrographs showing the effect of die size on the diameter of melt electrospun PP fibers fabricated by: (a) 0.2 trilobal (T) die; (b) 0.3 circular protruding (CP) die; (e) 0.3 circular (C) die; and (f) 0.2 CP die; diameter distribution plots of fibers fabricated by: (c) 0.2 T die; (d) 0.3 CP die; (g) 0.3 C die; and (h) 0.2 CP die.

It can be observed that the fibers fabricated by melt electrospinning of pure PP and PP with different additives are circular. Melt electrospinning of pure PP resulted in fibers of micrometer diameter. The inability to fabricate nanofibers in melt electrospinning can be attributed to the high viscosity of polymer melts, which is normally one order of magnitude higher than the viscosity of polymer solutions.12 Therefore, the shear

viscosity of the polymer melt was analyzed; the shear viscosity curves of PP with additives (7 wt% at 200 C) are shown in Figure 8. It was found that the shear viscosity of PP decreased in the presence of PEG and PDMS, while it increased with SO. Similar behavior was observed with adding the additives at 4 and 12 wt%. The decrease in the viscosity with the addition of PEG and PDMS resulted in the fabrication of finer

Nayak et al.

611

fibers with varying diameter (also refer to Figure 11). Although all the additives helped to reduce the fiber diameter, uniform nanofibers were fabricated only with the addition of SO. The results obtained from the rheological investigation showed that the viscosity of the polymer melt with the additive SO was increased. Hence, the other possibility for the fabrication of nanofibers is the increase in the electrical conductivity by the addition of SO. Therefore, the electrical conductivity of the polymer with SO was measured by an electrometer (Keithley

(a)

(b)

Figure 5. Electric field distribution patterns: (a) circular (C) die and (b) circular protruding (CP) die.

2612). Figure 9 shows the change in the electrical conductivity of PP with the addition of SO at 200 C. It can be observed from the figure that pure PP polymer showed electrical conductivity at the level of 10 12 S/cm at 200 C. It can be observed that, as the amount of additives increased from 4 to 12%, the electrical conductivity increased. The electrical conductivity increased from the level of 10 8 to 10 6 S/cm when the amount of SO increased from 4 to 12 wt%. Electrical conductivity in the polymer material is governed by the generation and mobility of the charge carriers or ions. The increase in the electrical conductivity with the addition of SO can be attributed to the effect of the ions from the dissociation of SO. During melt electrospinning, the ions increased the charge-carrying capacity of the polymer melt-jet. The melt-jet underwent whipping instability during its travel to the collector. The presence of more charges when SO was added increased the charge repulsion in the jet. Therefore, the whipping instability of the jet was increased and the jet was subjected to stronger stretching forces, resulting in the formation of finer fibers.21 In addition, the jet was repeatedly split into smaller jets by the increased charge density, resulting in smaller fiber diameter.2 As the addition of SO resulted in uniform nanofibers, an attempt was made to find out the optimum

Figure 6. Effect of die shape on the cross-section of the melt electrospun polypropylene fibers fabricated by (48 kV, 200 C and feed rate of 0.0013 ml/min): (a) circular die, (b) trilobal die, (c) tetralobal die and (d) multilobal die.

612

Textile Research Journal 83(6)

(a)

(b)

10 µm

10 µm (d) 10 0

AVG

: 3.39

80

SDEV

: 1.84

60

MIN

: 0.161

40

MAX

: 11 87

80 Frequency

Frequency

(c) 1 00

20

60 40

AVG

: 0.88

SDEV

: 0.61

MIN

: 0.14

MAX

: 3 54

20

0

0 0

2

4

6 8 10 12 14 16 18 20 F iber d iam e ter (μm )

(e)

0

2

4

6 8 10 12 14 16 18 20 F iber dia m e ter (μm )

(f)

10 µm

(h) 100

AVG

: 5.25

SDEV

: 2.37

60

MIN

: 1.1

40

MAX

: 13 86

80

60 40

AVG

: 1.49

SDEV

: 1.63

MIN

: 0.22

MAX

:90

20

20 0

80 Frequency

(g) 100

Frequency

10 µm

0

0

2

4

6 8 10 12 14 16 18 20 F iber diam eter (μm )

0

2

4 6 8 10 12 14 16 18 20 Fiber diameter (μm)

Figure 7. Scanning electron micrographs of melt electrospun polypropylene (PP) fibers with different additives (at 7 wt%, 48 kV, 200 C and a feed rate of 0.0013 ml/min): (a) pure PP; (b) PP with 7% sodium oleate (SO); (e) PP with 7% poly(ethylene glycol) (PEG); (f) PP with 7% poly(dimethyl siloxane) (PDMS); diameter distribution plots of the fibers: (c) pure PP; (d) PP with 7% SO; (g) PP with 7% PEG; (h) PP with 7% PDMS.

Nayak et al.

613

amount of SO for the fabrication of the lowest fiber diameter. The average diameters of the melt electrospun fibers with different amounts of SO were measured, the results of which are graphically shown in Figure 10. The figure shows that the smallest fiber diameter was achieved with 7 wt% SO. The average fiber diameter decreased up to 7 wt% of SO and then increased. When the amount of additives increased beyond this value, the fiber diameter started increasing. The increase in the conductivity after a certain level increased the instability of the melt electrospinning process and the formation of a larger Taylor cone. This led to the increase in the fiber diameter after a certain percentage of SO. The effects of different levels of additives on fiber diameter are shown graphically in Figure 11. It can be observed that in the case of pure PP and PP with PEG and PDMS, the average fiber diameter was in the micrometer range. Nanofibers were fabricated only in the case of SO. The effect of increasing the amount of additives from 4 to 12 wt% on fiber diameter shows a decrease followed by an increase trend in the case of SO. The fiber diameter increased when the PEG concentration was increased from 4 to 7 wt% and then decreased at 12 wt%. In case of PDMS, an increasing trend was observed when the PDMS concentration was increased from 4 to 12 wt%. It can also be observed from the figures that as the collector distance increased, the fiber diameter decreased. At a collector distance of 150 mm, in the case of pure PP and PP with PDMS, no fiber was fabricated. This can be attributed to the insufficient electrostatic drag at very high collector distance.

uniform distribution of the additives in the electrospun fiber.

Elemental composition analysis. The presence and distribution of SO and PDMS in the electrospun PP fiber were analyzed by EDX. EDX analysis cannot be used to uniquely identify the elements of PEG, as it is a long-chain polymer of carbon (C), hydrogen (H) and oxygen (O). In the EDX spectra (Figure 12), the elements observed in the electrospun fibers with SO were C, O, aluminum (Al) and Na. The presence of Na indicates the presence of SO in the fiber. The presence of Al can be attributed to the underlying aluminum foil used to collect the fibers, which was present during the EDX analysis. Similarly, the EDX spectra of electrospun PP fibers with PDMS (Figure 13) showed the presence of Si, which was due to the PDMS. Figures 12 and 13 also indicate the distribution of the additives in the electrospun PP fiber. The net counts of Na or Si indicate the amount of the respective additives (i.e. SO and PDMS) in the fiber. It can be observed that as the percentage of SO or PDMS increased, the amount of Na or Si increased, respectively. The EDX mappings also showed the

Mechanical properties. The mechanical properties of the single nanofibers were evaluated using the Chatillon tensile tester. Ten specimens were tested for the nanofibers fabricated from 1000 MFI PP with the additive SO (7%). Out of the 10 specimens, only 2 were able to break properly at the center (results are given in bold in Table 2); 2 samples were broken during specimen mounting and the remaining 6 samples slipped at the jaws instead of breaking. Figure 14 shows the load-elongation curve of a single nanofiber. The general shape of the load-elongation curve is similar to most of the textile fibers. Comparison of the breaking load of the fibers fabricated in this study with other results is not possible, as the fiber diameters are different and so are the test methods. For a general idea, the breaking strength of a commercial PP fiber is 16.31 cN,26 whereas in our study it is about 1.6 cN. The preparation of a single nanofiber for tensile testing was a tedious process. In addition, trying with different adhesives to prevent the jaw slippage was not successful.

1000 MFI

Shear viscosity, η (Pa.s)

100 Pure PP

PP+7% SO

PP+7% PEG

PP+7% PDMS

50

0

0

40

80

120

Shear rate (1/s)

Figure 8. Shear viscosity of polypropylene (PP) with different additives (7 wt%, 200 C). SO: sodium oleate; PEG: poly(ethylene glycol); PDMS: poly(dimethyl siloxane).

Applied voltage (V)

Conductivity (S/cm)

0 1.E-05 1.E-07

20

40

60 PP+12% SO PP+7% SO PP+4% SO

1.E-09

Pure PP

1.E-11 1.E-13

Figure 9. Change in the electrical conductivity with the addition of sodium oleate at 200 C. PP: polypropylene.

614

Textile Research Journal 83(6)

120 mm

140 mm

150 mm

6 4 2

10 10 0 PP

0 10 0 PP

0+

+

+ 00 10 PP

SO

SO %

SO 8%

7% +

10 00 PP

PP

SO

6% SO + 10 0

0

00 10 PP

Pu re P

P

+

10 00

4% SO

0

12 %

Fiber diameter (µm)

8

Concentration of SO (wt%)

(a)

8

Fiber diameter (µm)

Figure 10. Optimum concentration of sodium oleate (melt electrospinning was performed at 48 kV, 200 C and a feed rate of 0.0013 ml/min; the absence of bars in the graphs indicates no fibers being fabricated). PP: polypropylene.

6

Pure PP

4% SO

4% PEG

4% PDMS

4 2

0 120

140

150

Collector distance (mm) (b)

8 Pure PP

7% SO

7% PEG

7% PDMS

Fiber diameter (µm)

6

4

2

0

120

150

140

(c)

8

Fiber diameter (µm)

Collector distance (mm)

6

Pure PP

12% SO

12% PEG

12% PDMS

4 2 0 120

140

150

Collector distance (mm)

Figure 11. Effect of the amount of additives (sodium oleate (SO), poly(ethylene glycol) (PEG) and poly(dimethyl siloxane) (PDMS)) on the fiber diameter (melt electrospinning was performed at 48 kV, 200 C and a feed rate of 0.0013 ml/min): (a) 4%; (b) 7%; (c) 12% (the absence of bars in the graphs indicates no fibers being fabricated). PP: polypropylene.

Nayak et al.

615

Figure 12. Energy-dispersive X-ray (EDX) spectra of electrospun polypropylene (PP) fibers (48 kV, 200 C and a feed rate of 0.0013 ml/min) with (a) 0%, (b) 4%, (c) 7% and (d) 12% of sodium oleate (SO). EDX mapping of electrospun PP fibers with (e) 0%, (f) 4%, (g) 7% and (h) 12% of SO.

Figure 13. Energy-dispersive X-ray (EDX) spectra of electrospun polypropylene (PP) fibers (48 kV, 200 C and a feed rate of 0.0013 ml/min) with (a) 0%, (b) 4%, (c) 7% and (d) 12% of poly(dimethyl siloxane) (PDMS). EDX mapping of electrospun PP fibers with (e) 0%, (f) 4%, (g) 7% and (h) 12% of PDMS.

616

Textile Research Journal 83(6) EDX microanalysis also provided evidence of the uniform distribution of the additives in the fiber structure. Tensile tests were performed on single nanofibers with limited success, due to the problems in preparing fiber samples and successfully holding them in the jaws of the testing machine without slippage.

Table 2. Tensile properties of single nanofibers fabricated by melt electrospinning Sample no.

Elongation at break (%)

Breaking load (cN)

1 2 3 4 5 6 7 8 9 10

1.19 1.4 3.03

0.029 0.148 1.369

a

a

3.52 0.9 1.41 1.69 1.51

1.945 0.034 0.08 0.085 0.083

a

a

Acknowledgments The technical support from Muthu Pannirselvam and Mike Allan (Rheology and Materials Processing Centre, School of Civil, Environmental & Chemical Engineering, RMIT University); Phil Francis, Peter Rummel, Matthew Field and Frank Antolasic (School of Applied Sciences, RMIT University); Geraldine Van Lint (School of fashion & Textiles, RMIT University); Gary Peeters and Lance Nichols (MSE, CSIRO, Clayton); Mark Greaves, John Ward and (Scanning Electron Microscopy, Digital Imaging & Surface Analysis Facility of MSE, CSIRO, Clayton) Wendy Tian (MSE, CSIRO, Clayton); Liz Goodall and Winston Liew (Materials Characterisation Services of MSE, CSIRO, Clayton); Youssof Shekibi (ET, CSIRO, Clayton); and David Sutton and Peter Kouwenoord (Lyondellbasell) is gratefully acknowledged.

a

Broken during specimen loading.

1.6

Funding

Load (cN)

1.2

The authors gratefully acknowledge the financial support provided by RMIT University Higher Degree by Research Publications Award (HDRPA-2012).

0.8 0.4

References 0 0

1

2

3

4

Elongation

Figure 14. Load-elongation curve of a single nanofiber fabricated by melt electrospinning.

Conclusions Melt electrospinning of high MFI (1000 MFI) PP with different additives (SO, PEG and PDMS) has been successfully achieved. The addition of additives helped in lowering the fiber diameter. The fiber diameter was decreased by the addition of PEG and PDMS, due to the decrease in the melt viscosity. The most promising additive, SO, was effective in reducing the fiber diameter to the nanometer scale due to the increase in the electrical conductivity. Nanofibers with average diameter of 880 nm were obtained by adding SO. In addition, it was observed that there is no significant effect of die shape on the cross-sectional shape of the melt electrospun fibers. All the die shapes (i.e. trilobal, tetralobal, multilobal and circular) produced fibers with circular cross-sections. EDX microanalysis showed the presence of the additives in the fiber structure.

1. Zeng J, Chen X, Xu X, et al. Ultrafine fibers electrospun from biodegradable polymers. J Appl Polym Sci 2003; 89: 1085–1092. 2. Doshi J and Reneker DH. Electrospinning process and applications of electrospun fibers. J Electrostat 1995; 35: 151–160. 3. Burger C, Hsiao BS and Chu B. Nanofibrous materials and their applications. Annu Rev Mater Res 2006; 36: 333–368. 4. Sill TJ and Recum HA. Electrospinning: applications in drug delivery and tissue engineering. Biomaterials 2008; 29: 1989–2006. 5. Huang ZM, Zhang YZ, Kotaki M, et al. A review on polymer nanofibers by electrospinning and their applications in nanocomposites. Compos Sci Technol 2003; 63: 2223–2253. 6. Nayak R, Padhye R, Arnold L, et al. Production of novel surfaces by electrospinning. Acta Universitatis Cibiniensis 2011; 58: 128–138. 7. Liu Y, Deng R, Hao M, et al. Orthogonal design study on factors effecting on fibers diameter of melt electrospinning. Polym Eng Sci 2010; 50: 2074–2078. 8. Deng R, Liu Y, Ding Y, et al. Melt electrospinning of lowdensity polyethylene having a low-melt flow index. J Appl Polym Sci 2009; 114: 166–175. 9. Nayak R, Padhye R, Kyratzis IL, et al. Recent advances in nanofibre fabrication techniques. Textile Research Journal 2012; 82(2): 129–147.

Nayak et al. 10. Lyons J, Pastore C and Ko F. Developments in meltelectrospinning of thermoplastic polymers. Polym Preprint 2003; 44: 122–123. 11. Subbiah T, Bhat G, Tock R, et al. Electrospinning of nanofibers. J Appl Polym Sci 2005; 96: 557–569. 12. Zhou H, Green T and Joo Y. The thermal effects on electrospinning of polylactic acid melts. Polymer 2006; 47: 7497–7505. 13. Ogata N, Lu G, Iwata T, et al. Effects of ethylene content of poly (ethylene co vinyl alcohol) on diameter of fibers produced by melt electrospinning. J Appl Polym Sci 2007; 104: 1368–1375. 14. Ogata N, Yamaguchi S, Shimada N, et al. Poly (lactide) nanofibers produced by a melt electrospinning system with a laser melting device. J Appl Polym Sci 2007; 104: 1640–1645. 15. Lee S and Kay Obendorf S. Developing protective textile materials as barriers to liquid penetration using melt electrospinning. J Appl Polym Sci 2006; 102: 3430–3437. 16. Dalton P, Grafahrend D, Klinkhammer K, et al. Electrospinning of polymer melts: phenomenological observations. Polymer 2007; 48: 6823–6833. 17. Lyons J, Li C and Ko F. Melt-electrospinning part I: processing parameters and geometric properties. Polymer 2004; 45: 7597–7603. 18. Kong C, Jo K, Jo N, et al. Effects of the spin line temperature profile and melt index of poly(propylene) on melt-electrospinning. Polym Eng Sci 2009; 49: 391–396.

617 19. Xie M, Liu X and Li H. Influence of poly(ethylene glycol) containing additives on extrusion of ultrahigh molecular weight polyethylene/polypropylene blend. J Appl Polym Sci 2006; 100: 1282–1288. 20. Ryan KJ, Lupton KE, Pape PG, et al. Ultra high molecular weight functional siloxane additives in polymers: effects on processing and properties. J Vinyl Add Technol 2000; 6: 7–19. 21. Lin T, Wang H and Wang X. The charge effect of cationic surfactants on the elimination of fibre beads in the electrospinning of polystyrene. Nanotechnology 2004; 15: 1375. 22. Tsebrenko M, Rezanova N, Nikolaeva A, et al. Effect of sodium oleate addition on the morphology of polypropylene-co-polyamide blends. Polym Eng Sci 1999; 39: 1014–1021. 23. Machado A, Maia J, Canevarolo S, et al. Evolution of peroxide induced thermomechanical degradation of polypropylene along the extruder. J Appl Polym Sci 2004; 91: 2711–2720. 24. Liang S, Hu D, Zhu C, et al. Production of fine polymer powder under cryogenic conditions. Chem Eng Technol 2002; 25: 401–405. 25. Li D and Xia Y. Electrospinning of nanofibers: reinventing the wheel? Adv Mater 2004; 16: 1151–1170. 26. Racu C. Influence of physical and mechanical characteristics of polypropylene fibres used for bending with hemp upon the yarn characteristics. Technical University Iasi Romania, Textile Engineering Department, 2001.