Synthesis and characterization of zinc oxide nanoparticles: Application to textiles as UV-absorbers Article  in  Journal of Nanoparticle Research · January 2008 DOI: 10.1007/s11051-007-9318-3

CITATIONS

READS

419

8,140

4 authors, including: Pierandrea Lo Nostro

Piero Baglioni

University of Florence

University of Florence

121 PUBLICATIONS   4,554 CITATIONS   

523 PUBLICATIONS   10,957 CITATIONS   

SEE PROFILE

SEE PROFILE

Some of the authors of this publication are also working on these related projects:

Green formulations for European shale formations View project

Teaching View project

All content following this page was uploaded by Piero Baglioni on 19 December 2013. The user has requested enhancement of the downloaded file.

J Nanopart Res (2008) 10:679–689 DOI 10.1007/s11051-007-9318-3

RESEARCH PAPER

Synthesis and characterization of zinc oxide nanoparticles: application to textiles as UV-absorbers Alessio Becheri Æ Maximilian Du¨rr Æ Pierandrea Lo Nostro Æ Piero Baglioni

Received: 16 July 2007 / Accepted: 30 September 2007 / Published online: 30 October 2007  Springer Science+Business Media B.V. 2007

Abstract We report the synthesis and characterization of nanosized zinc oxide particles and their application on cotton and wool fabrics for UV shielding. The nanoparticles were produced in different conditions of temperature (90 or 150 C) and reacting medium (water or 1,2-ethanediol). A high temperature was necessary to obtain small monodispersed particles. Fourier transformed infrared spectroscopy (FTIR), transmission electron microscopy (TEM), and X-ray powder diffractometry (XRD) were used to characterize the nanoparticles composition, their shape, size and crystallinity. The specific surface area of the dry powders was also determined. ZnO nanoparticles were then applied to cotton and wool samples to impart sunscreen activity to the treated textiles. The effectiveness of the treatment was assessed through UV–Vis spectrophotometry and the calculation of the ultraviolet protection factor (UPF). Physical tests (tensile strength and elongation) were performed on the fabrics before and after the treatment with ZnO nanoparticles. Keywords Zinc oxide  Nanoparticle(s)  Textile  UV  UPF  Sunscreen  Nanocomposites  Dispersions A. Becheri  M. Du¨rr  P. Lo Nostro (&)  P. Baglioni Department of Chemistry and CSGI, University of Florence, 50019, Sesto Fiorentino, Florence, Italy e-mail: [email protected] URL: http://www.csgi.unifi.it/

Introduction The application of nanoparticles to textile materials has been the object of several studies aimed at producing finished fabrics with different performances. For example nano-Ag has been used for imparting antibacterial properties (Lee et al. 2003; Dura´n et al. 2007), nano-TiO2 for UV-blocking and self-cleaning properties (Xin et al. 2004; Fei et al. 2006; Qi et al. 2007) and ZnO nanoparticles for antibacterial and UV-blocking properties (Wang et al. 2004; Baglioni et al. 2003; Wang et al. 2005; Vigneshwaran et al. 2006). Inorganic UV blockers are more preferable than organic UV blockers (Riva et al. 2006; Scalia et al. 2006). In fact, zinc oxide and titanium dioxide are non-toxic and chemically stable under exposure to both high temperatures and UV. Furthermore, nanoparticles have a large surface areato-volume ratio that results in a significant increasing of the effectiveness in blocking UV radiation when compared to bulk materials (Yadav et al. 2006). The use of nanotechnology in the textile industry has increased rapidly. This is mainly due to the fact that conventional methods used to impart different properties to fabrics often do not lead to permanent effects, and will lose their functions after laundering or wearing. Nanoparticles can provide high durability for treated fabrics, with respect to conventional materials, because they possess large surface area and high surface energy that ensure better affinity for fabrics and lead to an increase in durability of the

123

680

textile functions. Washfastness is a particular requirement for textile and it is strongly correlated with the nanoparticles adhesion to the fibers. In order to increase the washfastness, the nanoparticles can be applied by dipping the fabrics in a solution containing a specific binder (Vigneshwaran et al. 2006; Yadav et al. 2006). Washfastness can be further improved with the formation of covalent bonding between nanoparticles and the fabrics surface. In these cases the excellent UV blocking properties are still maintained after 55 home laundering (Daoud and Xin 2004; Xin et al. 2004; Lu et al. 2006). Nanoparticle coating may affect other fabric properties like dyeing capacity, tensile strength, bursting strength, bending rigidity, air permeability (comfort) and fabric friction that play a crucial role in textile industries. Cotton fabrics treated with bulk-ZnO or nano-ZnO show different physical and mechanical properties. This reflects the improved properties of nano-sized particles with respect to conventional materials. Air permeability of the fabric is reduced when the coating process is carried out with bulk-ZnO, while it is improved when nano-ZnO is used. This basic difference has great consequences on the garment’s breathability, and eventually on the comfort of the treated fabrics. As opposed to bulk-ZnO coating, in the case of nano-ZnO treated fabric, the small size and uniform distribution of the particles results in a significant lowering of the friction (Yadav et al. 2006). Titania nanocoating slightly enhances bursting strength of treated cotton and the hand effect remains unchanged when compared to the untreated fabric. Again, this is mainly due to the nano-scaled structure of the titania layer (Xin et al. 2004). Zinc oxide is widely used in different areas because of its unique photocatalytic, electrical, electronic, optical, dermatological, and antibacterial properties (Turkoglu and Yener 1997; Pan et al. 2001; Arnold et al. 2003; Sawai 2003; Xiong et al. 2003; Behnajady et al. 2006; Li et al. 2006; Tang et al. 2006c). For these applications, the nanoparticles need to be dispersed homogeneously in the different matrices, and a number of new synthetic strategies have been developed in order to prevent particles agglomeration, and increase the stability of ZnO nanoparticles dispersions (Guo et al. 2000; Kwon et al. 2002; Wang et al. 2002; Liufu et al. 2004; Tang et al. 2006a; Tang et al. 2006b). Zinc oxide is actually one of the best biofriendly absorbers of UV radiation that mainly come on Earth

123

J Nanopart Res (2008) 10:679–689

from the Sun through the atmospheric ozone layer (Sato and Ikeya 2004). UV radiation is responsible for the generation of free radical species (Bednarska et al. 2000; Takeshita et al. 2006) that are supposed to participate in the development of various pathologies such as cancer, ageing, Alzheimer’s disease, inflammatory disorders, and so on (Liebler 2006). In order to decrease the health risks due to overexposure to UV radiation, the World Health Organization (WHO) has also recommended the use of loosefitting, full-length clothes with a high protection factor (Algaba et al. 2007). However most sportwear and light clothing commonly worn in the summertime do not guarantee an efficient shield against UV. The protection provided by fabrics depends on several parameters: fiber type, color, the presence of UV absorbers and additives, the porosity, thickness, mass per unit surface, other finishing processes and laundering, and the wearing conditions (stretched, dry or wet) (Gamblicher et al. 2002; Wang et al. 2005; Algaba et al. 2007). The present work addresses the synthesis and characterization of ZnO nanoparticles obtained through a homogeneous phase reaction between zinc chloride and sodium hydroxide at high temperature. In order to evaluate the effects of the experimental conditions on the particle size and morphology, the temperature (90 or 150 C) and the reaction medium (water or 1,2-ethanediol) were changed. The particles were then characterized, by evaluating their chemical composition through FTIR spectroscopy, their crystallinity through X-ray diffractometry, their shape and size via TEM microscopy, and the specific surface area. ZnO nanoparticles were then applied to cotton and wool fabrics in order to evaluate the sunscreen activity in the treated textiles through UV spectrophotometry. The thermal behavior of the fabrics was assessed through thermogravimetric analysis (DTGA), and the mechanical resistance was evaluated through tensile strength and elongation tests.

Experimental Synthesis ZnCl2 (min. 98%), NaOH (pellet min. 99%), 1,2ethanediol (min. 99.5%), and 2-propanol (min.

J Nanopart Res (2008) 10:679–689

99.5%) were purchased from Merck (Darmstadt, Germany). All products were used as received. Water was purified by a Milli-RO6 Plus Millipore Organex system (Resistance [ 18 MX cm). Zinc oxide nanoparticles were synthesized following a procedure reported elsewhere (Moroni et al. 2005). The synthesis was carried out at a high degree of supersaturation, in order to achieve a nucleation rate much greater than the growth rate (Ambrosi et al. 2001). ZnCl2 (5.5 g) was dissolved in 200 mL of water at 90 C in an oil bath. 16 mL of 5 M NaOH aqueous solution were added dropwise to the zinc chloride solution, with a gentle stirring over a period of 10 min at 90 C. The particles were separated from the supernatant dispersion by sedimentation. The supernatant solution was discarded, and the remaining suspension washed five times with distilled water to lower the concentration of NaCl below 10–6 M. Each time, the dilution ratio between the concentrated suspension and washing solution was about 1:10. The complete removal of NaCl from the suspension was checked with a solution of AgNO3. The purified particles were then peptized with 2propanol in an ultrasonic bath for 10 min at room temperature. The peptization process is necessary to disrupt the microagglomerates and release the nanounits of zinc oxide (Perez-Maqueda et al. 1998; Salvadori and Dei 2001). The particles were then collected by centrifugation at 6,000 rpm for 15 min. The washing procedure was repeated three times. Thermal treatment of the particles at 250 C for 5 h lead to the formation of ZnO. The synthesis in 1,2ethanediol (ED) was carried out in the same way, but at 150 C.

681

for 15 min at atmospheric pressure (dry heat). In order to evaluate the nanoparticles adhesion to the textile fibers, the treated fabrics were washed five times according to a standard method (UNI EN ISO 26330:1996). A model A1 Wascator Electrolux automatic laundry machine (internal drum diameter 51.5 cm, internal drum depth 33.5 cm, heating capacity 5.4 kW) was used, and the washing cycles were performed at 30 C, with an ECE phosphate reference detergent (B) without optical brighteners. The drying step was carried out on a horizontal flat surface. The fabric specimen were tested before and after the washing cycles via TEM and UV spectrophotometry.

UV absorption properties The UV-screen properties of the treated fabrics were investigated by absorption spectroscopy using a UV– Vis spectrophotometer (Perkin-Elmer Lambda 35, equipped with a 60-mm integrating sphere). The blank reference was air. The UV profiles of the untreated samples were compared to the spectra collected from the same fabrics treated with ZnO nanoparticles, and the effectiveness in shielding UV radiation was evaluated by measuring the UV absorption, transmission and reflection. Each measurement is the average of four scans obtained by rotating the sample by 90. The transmission data were used to calculate the UPF (ultraviolet protection factor) and the percent UV transmission, according to the following equations (Gamblicher et al. 2001, 2002): Rk2

Fabric treatments White wool and cotton fabrics, kindly provided by Grado Zero Espace (Florence, Italy), were used as received. The mass per unit surface was 146 g/m2 for cotton and 339 g/m2 for wool. The fabric samples were conditioned at constant relative humidity (33%) and temperature (20 C). The wool and cotton samples (10 cm · 10 cm) were soaked for 10 min in a 2-propanol dispersion of ZnO nanoparticles (5% w/w), under gentle magnetic stirring. The clothes were then squeezed to remove the excess dispersion, and dried in a oven at 130 C

UPF ¼

EðkÞ  SðkÞ dk

k1

Rk2

ð1Þ

EðkÞ  SðkÞ  TðkÞ dk

k1 k2 P

percent UV transmission ¼

Tð k Þ

k1

ð k2  k1 Þ

:

ð2Þ

E(k) is the relative erythemal spectral effectiveness, S(k) is the solar spectral irradiance in W m–2 nm–1, and T(k) is the spectral transmission of the specimen obtained from UV spectrophotometric experiments. The values of E(k) and S(k) were obtained from the National Oceanic and Atmospheric Administration

123

682

J Nanopart Res (2008) 10:679–689

database (NOAA). The UPF value was calculated for UV-A in the range 315–400 nm, and for UV-B in between 295 and 315 nm. The percent UV transmission, obtained from Eq. 2, was determined for UV-A and UV-B radiation from the transmission spectra of the fabric samples.

Thermogravimetric analysis was performed with an SDT 2960, series Q600 apparatus (TA Instruments, Milan, Italy). The temperature range was between 25 and 500 C, with a scan rate of 20 C/ min. All runs were performed with a nitrogen flux of 100 mL/min.

Physical and physico-chemical characterization

Results and discussion

Physical tests (tensile strength and elongation) of the treated fabrics were performed according to the standard methods (UNI EN ISO 13934-1:1999). The chemical composition of the synthesized materials was checked by FTIR spectroscopy with a Biorad FTS-40 spectrometer. The crystallinity was determined by XRD using a Bruker D8 Advance Xrays Diffractometer equipped with a Cu Ka ˚ ) source (applied voltage 40 kV, current (k = 1.54 A 40 mA). About 0.5 g of the dried particles were deposited as a randomly oriented powder onto a Plexiglass sample container, and the XRD patterns were recorded at angles between 20 and 80, with a scan rate of 1.5/min. The crystallite domain diameters (D) were obtained from XRD peaks according to the Scherrer’s equation (Jenkins and Snyder 1996):

Synthesis and characterization of ZnO nanoparticles



0:89  k DW  cos h

ð3Þ

where k is the wavelength of the incident X-ray beam ˚ for the Cu Ka), h is the Bragg’s diffraction (1.54 A angle, and DW the width of the X-ray pattern line at half peak-height in radians. The shape and size of the particles were obtained through TEM, using a Philips EM201C apparatus operating at 80 kV. The samples for TEM measurements were placed on carbon-coated copper grids (supplied by Agar Scientific Ltd, U.K.). The samples for TEM measurements were prepared from very diluted dispersions of the particles in 2-propanol. Surface area measurements were determined from BET on a Coulter SA 3100 surface area analyzer, under N2 flow. The ZnO-treated fabrics were analyzed through scanning electron microscopy (SEM), using a Stereoscan S360 Oxford–Cambridge. The samples were previously coated with a thin layer of gold deposited by sputtering under vacuum.

123

The results indicate that the experimental conditions greatly affect the morphology and size of the particles, prepared with the different procedures (see Table 1). In fact, increasing the reaction temperature from 90 C in water up to 150 C in 1,2ethanediol results in a significant lowering of the nanoparticles size and of their agglomeration number N, calculated as (Shvalagin et al. 2007): 4 q N ¼ pR3 NA 3 M

ð4Þ

where NA, R, q, and M are the Avogadro number, the radius of the nanoparticles, the density (5.47 · 106 g/m3) and the molecular weight (81.408 g mol–1) of zinc oxide, respectively. The values of N are reported in Table 1. Figure 1 shows the FTIR spectra of the synthesized nanomaterials. The spectrum of the material obtained from synthesis 1 (in water at 90 C; Fig. 1a) clearly shows the Zn-O absorption band near 430 cm–1. The peaks at 3,450 and 2,350 cm–1 indicate the presence of –OH and C=O residues, probably due to atmospheric moisture and CO2 respectively. The same spectrum was obtained from the nanomaterial produced via synthesis 2 (in 1,2ethanediol at 150 C, see Fig. 1b). TEM images of the ZnO nanoparticles are shown in Fig. 2. Nanoparticles are nearly spherical and quite monodisperse. However, there are some larger aggregates in the sample obtained from synthesis 1 (Fig. 2a), because of the high surface energy of ZnO nanoparticles that results in aggregation, especially when the synthesis is carried out in an aqueous medium. Particles obtained from synthesis 2 are more monodisperse and isolated than the particles obtained from synthesis 1. This result indicates a larger

J Nanopart Res (2008) 10:679–689

683

Table 1 Reaction conditions, crystallite diameter calculated according to Scherrer (Eq. 3), particles diameter (obtained by averaging more than 400 particles from TEM micrographs), specific surface area (As), and agglomeration number N (from Eq. 4) for the different samples #

Solvent

1

Water

2

1,2-Ethanediol

Crystallite diameter (nm)

Average diameter (nm)

As (m2/g)

90

19.25 ± 0.002

21 ± 5

24.8 ± 5%

2 · 105

150

9.61 ± 0.001

9±1

60.1 ± 5%

1.5 · 104

T (C)

100

transmittance (%)

a)

b) 50

0 4000

3000

2000

1000

-1

wavenumber (cm )

Fig. 1 FTIR spectrum of ZnO nanoparticles obtained from synthesis 1 (a: full line) and synthesis 2 (b: dotted line)

peptization yield for synthesis 2 (Fig. 2b) respect to synthesis 1, and it is confirmed by comparing the particles size distribution obtained from TEM micrographs (Fig. 3). The mean diameter of the particles in the dry powder was measured by averaging the size of a large number of particles ([400) from the analysis of TEM micrographs. The particles diameter

N

ranges between 12 and 38 nm for the material obtained according to synthesis 1 (Fig. 3a), and between 5 and 15 nm in the case of synthesis 2 (Fig. 3b). Figure 2b shows some halos surrounding the particles due to the retention of some diol, that remains adsorbed on the ZnO nanoparticles, and produces the tiny peaks at 2,850–2,920 cm–1 in the FTIR spectrum (see Fig. 1b). Figure 4 shows the XRD spectra of the ZnO nanomaterials. The spectra show well-defined peaks typical of ZnO in the crystal structure of zincite, according to the Joint Committee on Powder Diffraction Standard (JCPDS) card number 36-1451. This indicates crystallinity of the synthesized solids. Traditionally, the broadening of the peaks in the XRD patterns of solids is attributed to particle size effects (Jenkins and Snyder 1996). The mean crystallite size of a powder sample was estimated from the full width at half-maximum (FWHM) of the diffraction peak according to the Scherrer equation. An interesting feature is that the peaks from synthesis 2 (Fig. 4b) are broader than the peaks from synthesis 1 (Fig. 4a). This result suggests that the particles obtained from synthesis 2 are smaller than the particles obtained from synthesis 1, as confirmed by TEM micrographs (Fig. 2), and reflects the effects due to the

Fig. 2 TEM micrographs on the materials obtained from synthesis 1 (a) and synthesis 2 (b) after three peptizations

123

684

J Nanopart Res (2008) 10:679–689

(101)

3000

counts

(100) (002)

2000

(110)

a)

(103)

(102)

(112) (200)(201) (004)(202)

1000

b) 0 20

30

40

50 60 2θ (degrees)

70

80

Fig. 4 XRD patterns of the material obtained from (a) synthesis 1 and (b) synthesis 2 (Table 1)

loss of weight above 300 C with a maximum pyrolysis temperature at about 375 C. Untreated wool show a small weight loss between 25 and 100 C due to the release of moisture, and a consistent loss of weight above 200 C, with a maximum pyrolysis temperature at about 328 C (Fig. 5b). The treatment of cotton and wool fabrics with nanosized ZnO does not modify significantly their thermal stability and maximum pyrolysis temperature. Fig. 3 Mean particle size and particle distribution of nanocrystalline zinc oxide obtained from (a) synthesis 1 and (b) synthesis 2 (Table 1)

experimental conditions on the nucleation and growth of the crystal nuclei. The particles size calculated on the basis of Scherrer’s equation agrees quite well with the value obtained through TEM micrographs (Table 1). The specific surface areas obtained from BET experiments are 24.8 m2/g in the case of synthesis 1, and 60.1 m2/g in the case of synthesis 2, respectively (see Table 1). These data, agree very well with the expected values calculated from the particle diameters, within the experimental error, and confirm the effects induced by the experimental conditions on the nucleation and growth rates of the crystal nuclei. Thermal analysis Thermogravimetric analysis profiles are shown in Fig. 5. Untreated cotton (Fig. 5a) shows a consistent

123

Electron microscopy The surfaces of the treated fabrics were observed by SEM microscopy. In Fig. 6, SEM micrographs show the nanoscaled ZnO particles on cotton (a) and wool (b) samples. The nanoparticles are well dispersed on the fiber surface in both cases, although some aggregated nanoparticles are still visible. The particles size plays a primary role in determining their adhesion to the fibers: it is reasonable to expect that the largest particle agglomerates will be easily removed from the fiber surface, while the smaller particles will penetrate deeper and adhere strongly into the fabric matrix. SEM images (Fig. 6c, d) confirm that the large agglomerates are removed from the textile surface after washing. Instead, although the nanoparticles are not covalently grafted to the fabric materials, preliminary gravimetric essays show that more than 50% of their initial amount remains bound to the fibers surface after washing.

J Nanopart Res (2008) 10:679–689

685

deriv. weight (% /°C)

a) 2.0 1.5 1.0 0.5 0.0

320

360

400

temperature (°C)

d er i v . w e ig h t (% /° C )

b) 0.4

0.2

0.0 250

300

350

400

450

temperature (°C)

Fig. 5 First derivative weight loss as a function of temperature. (a) ( ) untreated cotton, (j) cotton + ZnO synthesis 1, ( ) cotton + ZnO synthesis 2. (b) ( )untreated wool, (.) wool + ZnO synthesis 1, and () wool + ZnO synthesis 2

¤



¤

Sunscreen activity of fabrics The solar UV radiation is actually composed of UVA (400–315 nm), UV-B (315–290 nm) and UV-C (290–200 nm). These radiations are present in natural

terrestrial sunlight in different amounts, due to the filtering activity of the upper atmosphere, and to local conditions (latitude, altitude, clouds, etc.). UV-C and most of UV-B are filtered by the ozone layer. UV spectra were performed on the untreated and treated fabrics, by measuring the absorbance, transmission and reflection (see Fig. 7). Untreated cotton does not absorb UV radiation (Fig. 7a) while untreated natural wool strongly absorbs in the UV region between 200 and 300 nm (Fig. 7b). The application of nanosized ZnO particles on the cotton fabric increases the absorption of UV light over the entire investigated UV spectrum. Higher values of UV absorbance were obtained when ZnO nanoparticles from synthesis 2 were applied on cotton (Fig. 7a). Similar results were obtained for the treated wool samples. The application of nanosized ZnO on wool fabric increases UV light absorbance in the region between 300 and 400 nm if compared to the untreated wool, in both cases (Fig. 7b). The results imply that the effectiveness in shielding UV radiation is due to the UV absorption capacity of ZnO nanoparticles on the fabrics surface. UV transmission and reflection spectra confirm these conclusions, as the ZnOtreated cotton and wool samples do not transmit or reflect the radiation over the entire UV spectrum (Fig. 7c, d, e and f).

Fig. 6 SEM images of ZnO nanoparticles from synthesis 1 on: cotton (a) and wool (b) before washing, cotton (c) and wool (d) after washing

123

686

¤

b) 1.5 Absorbance (a.u.)



a)1.2

Absorbance (a.u.)

Fig. 7 Absorption spectra (a, b), transmission spectra (c, d) and reflection spectra (e, f) of the fabric samples. ( ) untreated cotton, (j) cotton + ZnO synthesis 1, (m) cotton + ZnO synthesis 2, ( ) untreated wool, (.) wool + ZnO synthesis 1, and () wool + ZnO synthesis 2

J Nanopart Res (2008) 10:679–689

0.8

0.4

0

200

400

300

1.0

0.5

0.0 200

500

λ (nm)

c)

400

500

300

400

500

400

500

d)

120

60

% Transmittance

% Transmittance

300 λ (nm)

80

40

0

200

40

20

0 400

300

200

500

λ (nm)

λ (nm)

e)

f) 60

% R efl ect ance

% Reflectance

120

80

40

0 200

300

400

500

123

20

0 200

300

λ (nm)

λ (nm)

The values of the ultraviolet protection factor (UPF) and the percent of UV transmission for UV-A and UV-B ranges were calculated according to Eqs. 1 and 2, respectively, and are listed in Table 2. The data reflect the higher protection against UV radiation provided by the ZnO-treated fabrics, particularly for the cotton samples loaded with zinc oxide nanoparticles synthesized according to procedure 2, while in the case of wool the nanoparticles produced with the two different methodologies gave comparable results. Although the calculated UPF are significantly lower

40

than the standard values required for classifying the clothing as ‘‘excellent’’ in UV-shielding, however these results confirm the protection against UV radiation produced by the treatment with nanosized ZnO on the fabrics. This effect can be enhanced by: (1) (2) (3)

selecting a more compact fabric, selecting another kind of textile material (polyester, viscose, etc.), using a different procedure for curing the fabric with the ZnO dispersion,

J Nanopart Res (2008) 10:679–689

687

Table 2 UPF (Eq. 1) and percent UV transmission (Eq. 2) for the different samples for UV-A (315–400 nm) and UV-B (295– 315 nm) radiation Sample

UPF UV-A

UV transmission (%) UV-B

UV-A/UV-B

UV-A

UV-B

Cotton Untreated

1.05

1.07

97.1

92.5

1.05

Synthesis 1

4.92

5.23

33.6

19.2

1.75

Synthesis 2

8.45

10.29

27.0

9.8

2.75

Wool Untreated

4.30

10.34

34.6

9.1

3.80

Synthesis 1

14.49

21.78

14.9

4.5

3.31

Synthesis 2

13.49

21.42

15.5

4.6

3.37

Table 3 Tensile strength (N) and elongation (%) of the different samples Sample

samples is higher than that of the untreated specimen (see Table 3). This effect could be related to the peculiar behavior of wool fabrics in the presence of aqueous environments (shrinkage), and particularly in alkaline conditions, that lower its resistance and deteriorate its structural properties.

Maximum force (N)

Elongation (%)

Warp

Weft

Warp

Weft

Untreated

541

690

14.90

14.60

Synthesis 1

629

719

14.24

13.60

Synthesis 2

682

674

13.84

13.85

Conclusions

Untreated Synthesis 1

661 689

487 548

15.45 20.44

12.90 18.50

Synthesis 2

710

576

29.14

21.15

We report the synthesis of zinc oxide nanoparticles through a homogeneous phase reaction starting from zinc chloride and sodium hydroxide at high temperature, in water or in 1,2-ethanediol. The reaction in 1,2-ethanediol at 150 C results in the formation of smaller nanoparticles with respect to the reaction carried out in water at 90 C. In both cases, the nanoparticles appear to be nearly spherical and with a quite narrow size range. Nanoparticles were analyzed through electron microscopy, X-ray diffraction, FTIR, and specific surface area experiments. The homogeneous phase reaction processes offer a valid alternative for an industrial-scale production of ZnO nanoparticles for many applications. The peculiar performance of ZnO nanoparticles as UV-absorbers, can be efficiently transferred to fabric materials through the application of ZnO nanoparticles on the surface of cotton and wool fabrics. The UV tests indicate a significant increment of the UV absorbing activity in the ZnO-treated fabrics. Such result can be exploited for the protection of the body against solar radiation and for other technological applications.

Cotton

Wool

(4)

spreading an appropriate filming additive on the fabric in order to increase the amount of zinc oxide embedded into the textile structure.

Mechanical properties The application of ZnO nanoparticles on cotton increases the mechanical strength of the fabric, especially in the warp direction, and decrease their elongation if compared to the untreated cotton (see Table 3). Probably the treated fabric is stiffer than the untreated specimen, and this results in a higher maximum force and lower elasticity. In the case of wool, the application of ZnO nanoparticles increases the maximum force, both in the warp and weft direction. However, the elongation of treated wool

123

688

Further studies are currently being carried out in order to enhance the UV-shielding activity of ZnOloaded textiles. Acknowledgments The authors greatly acknowledge partial financial support from CSGI (Florence, Italy) and MIUR (PRIN-2003, Rome, Italy).

References Algaba IM, Pepio´ M, Riva A (2007) Modelization of the influence of the treatment with two optical brighteners on the ultraviolet protection factor of cellulosic fabrics. Ind Eng Chem Res 46:2677–2682 Ambrosi M, Dei L, Giorgi R, Neto C, Baglioni P (2001) Colloidal particles of Ca(OH)2: properties and applications to restoration of frescoes. Langmuir 17:4251–4255 Arnold MS, Avouris P, Pan ZW, Wang ZL (2003) Field-Effect transistors based on single semiconducting oxide nanobelts. J Phys Chem B 107:659–663 Baglioni P, Dei L, Fratoni L, Lo Nostro P, Moroni M (2003) Preparation of nano- and micro-particles of group II and transition metals oxides and hydroxides and their use in the ceramic, textile and paper industries. Patent WO 2003082742 Bednarska K, Wachowicz B, Buczynski A (2000) UVB-induced generation of free radicals in blood platelets. J Photochem Photobiol B: Biology 55:109–112 Behnajady MA, Modirshahla N, Hamzavi R (2006) Kinetic study on photocatalytic degradation of C.I. acid yellow 23 by ZnO photocatalyst. J Hazardous Mat 133:226– 232 Daoud WA, Xin JH (2004) Low temperature sol-gel processed photocatalytic titania coating. J Sol-Gel Sci Technol 29:25–29 Dura´n N, Marcato PD, De Souza GIH, Alves OL, Esposito E (2007) Antibacterial effect of silver nanoparticles produced by fungal process on textile fabrics and their effluent treatment. J Biomed Nanotechnol 3:203–208 Fei B, Deng Z, Xin JH, Zhang Y, Pang G (2006) Room temperature synthesis of rutile nanorods and their applications on cloth. Nanotechnology 17:1927–1931 Gambichler T, Avermaete A, Bader A, Altmeyer P, Hoffmann K (2001) Ultraviolet protection by summer textiles. Ultraviolet transmission measurements verified by determination of the minimal erythema dose with solarsimulated radiation. Br J Dermatol 144:484–489 Gambichler T, Hatch KL, Avermaete A, Altmeyer P, Hoffmann K (2002) Influence of wetness on the ultraviolet protection factor (UPF) of textiles: in vitro and in vivo measurements. Photodermatol Photoimmunol Photomed 18:29–35 Guo L, Yang S, Yang C, Yu P, Wang J, Ge W, Wong GKL (2000) Synthesis and characterization of poly(vinylpyrrolidone)-modified zinc oxide nanoparticles. Chem Mater 12:2268–2274 Jenkins R, Snyder RL (1996) Introduction to X-ray powder diffractometry. John Wiley & Sons, New York

123

J Nanopart Res (2008) 10:679–689 Kwon YJ, Kim KH, Lim CS, Shim KB (2002) Characterization of ZnO nanopowders synthesized by the polymerized complex method via an organochemical route. J Ceramic Proc Res 3:146–149 Lee HJ, Yeo SY, Jeong SH (2003) Antibacterial effect of nanosized silver colloidal solution on textile fabrics. J Mater Sci 38:2199–2204 Li YQ, Fu SY, Mai YM (2006) Preparation and characterization of transparent ZnO/epoxy nanocomposites with highUV shielding efficiency. Polymer 47:2127–2132 Liebler DC (2006) The poisons within: application of toxicity mechanisms to fundamental disease processes. Chem Res Toxicol 19:610–613 Liufu S, Xiao H, Li Y (2004) Investigation of PEG adsorption on the surface of zinc oxide nanoparticles. Powder Technol 145:20–24 Lu H, Fei B, Xin JH, Wang RH, Li L (2006) Fabrication of UV-blocking nanohybrid coating via miniemulsion polymerization. J Colloid Interface Sci 300:111–116 Moroni M, Borrini D, Calamai L, Dei L (2005) Ceramic nanomaterials from aqueous and 1,2-ethanediol supersaturated solutions at high temperature. J Colloid Interface Sci 286:543–550 National Oceanic and Atmospheric Administration (NOAA)/ National Weather Service, Climate Prediction Center web site: http://www.cpc.ncep.noaa.gov/products/stratosphere/ uv_index/gif_files/spectrum.gif. Cited 16 July 2007 Pan ZW, Dai ZR, Wang ZL (2001) Nanobelts of semiconducting oxides. Science 291:1947–1949 Perez-Maqueda LA, Wang L, Matijevic E (1998) Nanosize indium hydroxide by peptization of colloidal precipitates. Langmuir 14:4397–4401 Qi K, Chen X, Liu Y, Xin JH, Mak CL, Daoud WA (2007) Facile preparation of anatase/SiO2 spherical nanocomposites and their application in self cleaning textiles. J Mater Chem 17:3504–3508 Riva A, Algaba IM, Pepio´ M (2006) Action of a finishing product in the improvement of the ultraviolet protection provided by cotton fabrics. Modelisation of the effect. Cellulose 13:697–704 Salvadori B, Dei L (2001) Synthesis of Ca(OH)2 nanoparticles from diols. Langmuir 17:2371–2374 Sato H, Ikeya M (2004) Organic molecules and nanoparticles in inorganic crystals: vitamin C in CaCO3 as an ultraviolet absorber. J Appl Phys 95:3031–3036 Sawai J (2003) Quantitative evaluation of antibacterial activities of metallic oxide powders (ZnO, MgO and CaO) by conductimetric assay. J Microbiol Methods 54:177–182 Scalia S, Tursilli R, Bianchi A, Lo Nostro P, Bocci E, Ridi F, Baglioni P (2006) Incorporation of the sunscreen agent, octyl methocycinnamate in a cellulosic fabric grafted with b-cyclodextrin. Int J Pharm 308:155–159 Shvalagin VV, Stroyuk AL, Kuchmii SYa (2007) Photochemical synthesis of ZnO/Ag nanocomposites. J Nanopart Res 9:427–440 Takeshita K, Chi C, Hirata H, Ono M, Ozawa T (2006) In vivo generation of free radicals in the skin of live mice under ultraviolet light, measured by L-band EPR spectroscopy. Free Radic Biol Med 40:876–885 Tang E, Cheng G, Ma X (2006a) Preparation of nano-ZnO/ PMMA composite particles via grafting of the copolymer

J Nanopart Res (2008) 10:679–689 onto the surface of zinc oxide nanoparticles. Powder Technol 161:209–214 Tang E, Cheng G, Ma X, Pang X, Zhao Q (2006b) Surface modification of zinc oxide nanoparticle by PMAA and its dispersion in aqueous system. Appl Surf Sci 252:5227– 5232 Tang E, Cheng G, Pang X, Ma X, Xing F (2006c) Synthesis of nano-ZnO/poly(methylmethacrylate) composite microsphere through emulsion polymerization and its UVshielding property. Colloid Polym Sci 284:422–428 Turkoglu M, Yener S (1997) Design and in vivo evaluation of ultrafine inorganic-oxide-containing-sunscreen formulations. Int J Cosmet Sci 19:193–201 UNI EN ISO 13934-1:1999—Tensile properties of fabrics. Part 1: determination of maximum force and elongation at maximum force using the strip method UNI EN ISO 26330:1996—Domestic washing and drying procedures for textile testing Vigneshwaran N, Kumar S, Kathe AA, Varadarajan PV, Prasad V (2006) Functional finishing of cotton fabrics using zinc oxide-soluble starch nanocomposites. Nanotechnology 17:5087–5095

689 Wang Y, Ma C, Sun X, Li H (2002) Preparation of nanocrystalline metal oxide powders with the surfactantmediated method. Inorg Chem Comm 5:751–755 Wang RH, Xin JH, Tao XM, Daoud WA (2004) ZnO nanorods grown on cotton fabrics at low temperature. Chem Phys Lett 398:250–255 Wang RH, Xin JH, Tao XM (2005) UV-blocking property of dumbbell-shaped ZnO crystallites on cotton fabrics. Inorg Chem 44:3926–3930 Xin JH, Daoud WA, Kong YY (2004) A new approach to UV-blocking treatment for cotton fabrics. Text Res J 74:97–100 Xiong M, Gu G, You B, Wu L (2003) Preparation and characterization of poly(styrene butylacrylate) latex/nano-ZnO nanocomposites. J Appl Polym Sci 90:1923–1931 Yadav A, Prasad V, Kathe AA, Raj S, Yadav D, Sundaramoorthy C, Vigneshwaran N (2006) Functional finishing in cotton fabrics using zinc oxide nanoparticles. Bull Mater Sci 29:641–645

123 View publication stats